Mechanical properties
Profiles EN 755 - 2 / DIN 1748
| State | dimensions in mm wall thickness | Tensile strenght Rm Mpa | 0,2 Yield stress Rp0,2 Mpa | Tensile A% |
A50% |
||||||
| En | Din | Active ingredient nr. | En | Din | Min. | Max. | Min. | Max. | Min. | Max. | |
| 5754 (AlMg3) | AlMg3 | 3.3535,08 | H112,F | F18 | <25 | 180 | - | 80 | - | 14 | 12 |
| 5083 (AlMg4,5Mn0,7) |
AlMg4,5Mn |
3.3547,08 | H112 | F27 | alle | 270 | - | 125 | - | 12 | 10 |
| 6005 (AlSiMg) |
AlMgS10,7 | 3.3210,71 |
T6 | F26/F27 | gesloten <5 | 270 | - | 225 | - | 8 | 6 |
| |
5 - 10 |
260 | - | 215 | - | 8 | 6 | ||||
| |
10 - 25 |
250 |
- | 200 | - | 8 | 6 | ||||
| |
buisprof. <5 | 255 | - | 215 | - | 8 | 6 | ||||
| |
5 - 15 |
250 | - | 200 | - | 8 | 6 | ||||
| 6060 (AlMgSi) |
AlMgSi0,5 | 3.3206,51 | T4 | F13 zacht |
<15 | 120 | - | 60 | - | 16 | 14 |
| - | T64 | F18 buigkwaliteit |
<15 | 180 | - | 120 | - | 12 | 10 | ||
| |
3.3206,71 | T6 | F22 | <3 | 190 | - | 150 | - | 8 | 6 | |
| 3 - 25 | 170 | - | 140 | - | 8 | 6 | |||||
| |
|
3.3206,71 | T66 | F22 | <3 | 215 | - | 160 | - | 8 | 6 |
| |
3 - 25 | 195 | - | 150 | - | 8 | 6 | ||||
| 6061 (AlMg1SiCu) |
AlMg1SiCu |
3.3211,71 | T6 | F29 | <5 | 260 | - | 240 | - | 9 | 7 |
| |
5 - 25 | 260 | - | 240 | - | 10 | 8 | ||||
| 6082 (AlSi1MgMn) |
AlMgSi1 | 3.2315,71 | T6 |
F28 | <5 | 290 | - | 250 | - | 8 | 6 |
| |
3.2315,72 | T6 | F31 | 5 - 25 | 310 | - | 260 | - | 10 | 8 |
Bars EN &55 - 2 / DIN 1748
| State | dimensions in mm wall thickness | Tensile strenght Rm Mpa | 0,2 Yield stress Rp0,2 Mpa | Tensile A% |
A50% |
||||||
| En | Din | Active ingredient nr. | En | Din | Min. | Max. | Min. | Max. | Min. | Max. | |
| 2007 (AlCu4PbMgMn) | AlCuMgPb | 3.1645,51 | T4 | F37 | <80 | 370 | - | 250 | - | 8 | 6 |
| 80 - 200 | 340 | - | 220 | - | 8 | - | |||||
| 200 - 250 | 330 | - | 210 | - | 7 | - | |||||
| 2011 (AlCu6SiPb) | AlMgBiPb | 3.1655,51 | T4 | F28-F32 | <200 | 275 | - | 125 | - | 14 | 12 |
| 71 |
T6 | F37 | <75 | 310 |
- | 230 | - | 8 | 6 | ||
| 75 - 200 | 295 | - | 195 | - | 6 | - | |||||
| 5754 (AlMg3) | AlMg3 | 3.3535,08 | H112,F | F18 | <150 | 180 | - | 80 | - | 14 | 12 |
| 150 - 250 | 180 | - | 70 | - | 13 | - | |||||
| 5083 (AlMg4,5Mn0,7) | AlMg4,5Mn | 3.3547,08 | H112,F | F27 | <200 | 270 | - | 110 | - | 12 | 10 |
| H111 | 200 - 250 | 260 | - | 100 | - | 12 | - | ||||
| 0 | - | <200 | 270 | - | 125 | - | 12 | 10 | |||
| 6060 (AlMgSi) | AlMgSi0,5 | 3.3206,71 | T6 (6) | F22 | <150 | 215 | - | 160 | - | 8 | 6 |
| 6082 (AlSiMgMn) | AlMgSi1 | 3.2315,71 | T6 | F27-F31 | <20 | 295 | - | 250 | - | 8 | 6 |
| 72 | 20 - 150 | 310 | - | 260 | - | 5 | - | ||||
| 150 - 200 | 280 | - | 240 | - | 6 | - | |||||
| 200 - 250 | 270 | - | 200 | - | 6 | - | |||||
| 7020 (AlZn4,5Mg1) | AlZn4,5Mg1 | 3.4335,71 | T6 | F35 | <50 | 350 | - | 290 | - | 10 | 8 |
| 50 - 20 0 | 340 | - | 275 | - | 10 | - | |||||
| 7075 (AlZn5,5MgCu) | AlZnMgCu1,5 | 3.4365,71 | T6 | F50<F52 | <25 | 540 | - | 480 | - | 7 | 5 |
| 25 - 100 | 560 | - | 500 | - | 7 | - | |||||
| 100 - 150 | 530 | - | 470 | - | 6 | - | |||||
| 150 - 200 | 470 | - | 400 | - | 5 | - |